heat vs bricks

Postby motorhead fan » Sun Dec 01, 2013 3:41 pm

1 question: does heat give minifigs cracked arms and legs? ( i don't mean fire i mean stuff like underfloor heating)
<Motorheadfan>: Paper cuts for everyone!
User avatar
motorhead fan
mine is one or two inches longer now
Posts: 1206
Joined: Sat Jul 20, 2013 9:17 am
Location: Switzerland

Re: heat vs bricks

Postby Overwatch_Elite » Sun Dec 01, 2013 4:08 pm

I highly doubt the heating in the house would interfere with what you put on the floor. Even then, I'm almost positive that if anything caused your lego's to crack it would be the cold.

Then again I failed science so you should probably get colette or something he knows alot of stupid shit
User avatar
Posts: 1406
Joined: Sat Oct 13, 2012 3:31 pm

Re: heat vs bricks

Postby Battlegrinder » Sun Dec 01, 2013 7:08 pm

Rapid heating and cooling can make some materials brittle, but generally you'd need to heat a substance to the point that it's nearly melted in order to risk damage from cooling it back down. So unless your floor gets hot enough to melt plastic, you should be fine (and if it does, you have bigger problems than a few melted minifigs).
"There's suspension of disbelief and then there's insulting my fucking intelligence"
Noah Antwiler
User avatar
Posts: 803
Joined: Tue May 01, 2012 5:52 pm
Location: Quincy, Illinois

Re: heat vs bricks

Postby Gungnir » Sun Dec 01, 2013 9:03 pm

Maybe if you put them right on the heater. But why would you do that?
Are you sure it's not your dog again?
Give a minifig an inch, and he'll murder for a mile.
User avatar
Posts: 805
Joined: Wed Jul 14, 2010 3:01 am

Re: heat vs bricks

Postby Scribonius » Sun Dec 01, 2013 9:48 pm

Um... heat usually doesn't, but every now and then Lego gets a shipment of plastic pellets with some kind of impurity in them that causes the plastic to develop cracks over time during normal use - the cracks are usually along seam lines, but sometimes right in the middle of a flat surface. Several of the original Pirate sets that I got when I was a kid developed cracks like those. Doesn't happen often, but it does happen. Could also be from the plastic cooling too quickly during casting so it doesn't "meld" properly...
User avatar
Posts: 198
Joined: Thu Jul 23, 2009 9:29 pm
Location: Wandering through Mirial's Rock...

Re: heat vs bricks

Postby Tzan » Sun Dec 01, 2013 11:11 pm

Scribonius wrote: it doesn't "meld" properly...

That's what Sarek said,
when talking about his overly emotional, halfbreed son.
User avatar
Posts: 5380
Joined: Sun Dec 30, 2007 4:41 pm
Location: Boston

Re: heat vs bricks

Postby Zahru II » Mon Dec 02, 2013 4:42 am

Could also be from the plastic cooling too quickly during casting so it doesn't "meld" properly...

Yup, that's what happened to the majority of lime colored bonkle connector pieces in 2007. Those things were brittle as shit, cracking and breaking after the first attaching/detaching.

My stuff: Medivo / Armylists / Battles / SPACE
User avatar
Zahru II
Posts: 4802
Joined: Fri Jul 24, 2009 6:22 am
Location: Hüngäry

Re: heat vs bricks

Postby samuelzz10 » Mon Dec 02, 2013 8:51 pm

Unless you leave legos in the trunk of a car with your dead bodies during the middle of summer, heat wont ruin your legos.
Spoiler: show
my old sig

WARNING: Posts in forum may have been edited by forum
User avatar
Posts: 1540
Joined: Sun Oct 04, 2009 7:09 pm
Location: planet express

Re: heat vs bricks

Postby Bluefog » Tue Dec 03, 2013 6:04 am

Don't put lego on the floor. Haven't you ever in your life stepped on one?
"Do be careful! Don't lose any of that stuff. That's concentrated evil. One drop of that could turn you all into hermit crabs."
User avatar
Cannon Fodder
Posts: 325
Joined: Mon Feb 18, 2013 3:11 am
Location: Over there.

Re: heat vs bricks

Postby Kaplan » Thu Dec 05, 2013 2:43 am

I think this is a question I could answer correctly.
As much as I know thermal cracking of ABS could occur right after the manufacture process when hot plastic cooled down but reheating could not lead the parts to crack.